CR ASIA (India) CO.,LTD.
802, Windfall,Sahar Plaza,J.B. Nagar, Andheri(east),Mumbai-400 059 Tel : (91-22) 65701556-57 Fax : (91-22) 26821317 www.crasia.net
WELDING PROCEDURE SPECIFICATION (WPS) WPS No. : WPS-P15-H-01 (Page 1 of 2)
WRITTEN BY : VISHAL SUPPORTING P.Q.R.( PQR-P15-H-01 WPS REVISION No. 0 WELDING PROCESS GTAW
DATE :
12/2/2016
DATE : TYPE :
Manual
ALL WELDING SHALL BE IN ACCORDANCE WITH, ASME IX & ASME/ ANSI B31.3
JOINT (QW-402)
JOINT DESIGN As Per Drawing BACKING : NA BACKING MATERIAL( NA (REFER TO BOTH BACKING AND RETAINERS)
P.No. :
25
BASE METAL (QW-403)
GROUP No. :
NA
TO
P #N##
GROUP No. :
OR
SPECIFICATION AND TYPE / SB 241 A95083 TO SPECIFICATION AND TYPE / SB 241 A95083 THICKNESS RANGE : 6 BASE METAL GROOVE11.08 FILLET All PIPE DIA. RANGE GROOVE 1' to Unlimited FILLET All OTHER joint design is non-essential varbiale so any change in it do not require to prepare pqr separatly
FILLER METAL (QW-404) WELD PASS(ES) GTAW SMAW SPEC. No. (SFA) 5.1 5.1 AWS No.(CLASS) ER5183 ER5183 F-No. F22 F22 A-No. NA NA TRADE NAME Esab, D&Esab, H D& H SIZE OF FILLER METALS 1.6 mm 1.6 mm Deposited weld metal : Electrode Flux (Class) bare solidcoated wire electrode Flux Trade Name Consumable Insert WELD METAL THICKNESS R GROOVE 4.12mm max 7 max FILLET all all
Other :
PREPARED BY : CRAI QA/QC
F-QC-33 Rev.00
WITHNESSED & CERTIFIEDAPPROVED BY : CLIENT
Issue date : June 19, 2006
SIGNATURE :
SIGNATURE :
SIGNATURE :
NAME : DATE :
NAME : DATE :
NAME : DATE :
F-QC-33 Rev.00
Issue date : June 19, 2006
CR ASIA (India) CO.,LTD.
802, Windfall,Sahar Plaza,J.B. Nagar, Andheri(east),Mumbai-400 059 Tel : (91-22) 65701556-57 Fax : (91-22) 26821317 www.crasia.net
WELDING PROCEDURE SPECIFICATION (WPS) WPS No. : WPS-P15-H-01 (Page 2 of 2)
POSITION (QW-405)
POST WELD HEAT TREATMENT (QW-407
PREHEAT (QW-406)
GAS (QW-408)
POSITION(S) GROOVE 6 G WELDING PROGRESSIOUPHILL/ forehand POSITION(S) FILLET All
PREHEAT TEMP.MIN. ambient (26 c) INTERPASS TEMP. MAXNA PREHEAT MAINTENANNA
TEMPERATURE RANG NA HEATING CYCLE NA SOAK PERIOD NA
SHIELDING GAS(ES) COMPOSITION FLOW RATE GAS BACKING
Argon 99.99% 9.4-11.8 Ltr/ Min NA
ELECTRICAL CHARACTERISTIC (QW-409) CURRENT(AC OR DC) AC POLARITY Straight & Reverse AMPS (RANGE) 60-450 VOLTS (RANGE) 10-20 Electrode Wire Feed Speed Rate : TUNGSTEN ELECTRODE (SIZE AND2.4 mm Tugstan 2% Throated or EW Th2
Mode Of Metal Transfer : WELD FILLER METAL PROCESS LAYER CLASS DIA Root Hot
Fill up Final
GTAW GTAW GTAW GTAW
ER5183 ER5183 ER5183 ER5183
1.6 1.6
2.4 2.4
CURRENT
VOLT
POLARITY RANGE AMP RANGE AC AC
AC AC
60-80 60-80
10-15 10-15
125-160 125-160
heat inputSPEED(mm
15-20 15-20
TECHNIQUE (QW-410)
STRING OR WEAVE BERoot Pass stringer , Fill Up & Final weave bead ORIFICE OR GAS CUP S6.5mm/13mm Multiple or Single electrode Travel Speed (ran: mm/min Peening
Method Of Back Gouging Oscillation :
Initial or interpass cleaning : Other :
PREPARED BY : CRAT QA/QC F-QC-33 Rev.00
TRAVE
APPROVED BY : CLIENT
Issue date : June 19, 2006
50-55 50-55 50-55 50-55
SIGNATURE :
SIGNATURE :
NAME : DATE :
NAME : DATE :
F-QC-33 Rev.00
Issue date : June 19, 2006
RE SPECIFICATION (WPS) -P15-H-01 (Page 1 of 2)
ACCORDANCE WITH, ASME IX & ASME/ ANSI B31.3
T (QW-402)
TAL (QW-403)
NA
ETAL (QW-404)
F-QC-33 Rev.00
Issue date : June 19, 2006
F-QC-33 Rev.00
Issue date : June 19, 2006
RE SPECIFICATION (WPS) -P15-H-01 (Page 2 of 2)
OST WELD HEAT TREATMENT (QW-407)
GAS (QW-408)
RACTERISTIC (QW-409)
TRAVEL
SPEED(mm/mm) 50-55 50-55
QUE (QW-410)
F-QC-33 Rev.00
50-55 50-55
Issue date : June 19, 2006
F-QC-33 Rev.00
Issue date : June 19, 2006